System
|
Type
|
Thickness (mm)
|
Electrolyte resistance* (Ω cm2)
|
Expansion (%)
|
Alkaline absorption (%)
|
Dry tensile strength( N / cm2)
|
Typical applications
|
|
MD
|
TD
|
MD
|
TD
|
|
Grafted
membrane
(PE)
|
CN-1000
|
0.020±0.005
|
0.05~0.07
|
-3~5
|
-3~5
|
≧150
|
≧700
|
≧500
|
High drain’s secondary vented Ni/Cd
|
|
CN-2000
|
0.030±0.008
|
0.06~0.09
|
-3~5
|
-3~5
|
≧150
|
≧700
|
≧500
|
High drain’s secondary Zn/Ag2O
|
|
CN-2020(3)
|
0.030±0.008
|
0.07~0.12
|
-3~5
|
-3~5
|
≧150
|
≧700
|
≧500
|
Medium & low drain’s secondary vented Ni/Cd
|
|
SL-060(1)
|
0.010±0.003
|
0.04~0.06
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
High drain’s secondary vented Ni/Cd & motive secondary Zn/Air
|
|
SL-080(1)
|
0.015±0.005
|
0.06~0.09
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
Medium drain’s secondary vented Ni/Cd & secondary Zn/Air
|
|
SL-080(5)
|
0.015±0.005
|
0.08~0.16
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
Medium drain’s secondary Zn/Ag2O
|
|
SL-080(7)
|
0.015±0.005
|
0.10~0.20
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
Low drain’s secondary Zn/Ag2O
|
|
AS-CN1
|
0.020±0.005
|
0.04~0.06
|
-3~5
|
-3~5
|
≧150
|
≧700
|
≧500
|
Secondary motive Zn/Air & super capacitor
|
|
AS-SL6
|
0.010±0.003
|
0.04~0.06
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
|
AS-SL8
|
0.015±0.005
|
0.05~0.07
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
|
PPF-A
|
0.028±0.005
|
0.12~0.15
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
Super Capacitor
|
|
AS-CN1-7
|
0.07±0.01
|
0.16~0.22
|
-3~5
|
-3~5
|
≧150
|
≧700
|
≧500
|
Secondary motive Zn/Air & super capacitor
|
|
AS-SL8-7
|
0.07±0.01
|
0.15~0.20
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
|
Laminated
membrane
|
PPAT-CN1(2)
|
0.18±0.04
|
0.12~0.15
|
-3~5
|
-5~5
|
≧400
|
≧400
|
≧300
|
High capacity secondary vented Ni/Cd, and secondary Zn/Ag2O & super capacitor
|
|
PPAT-SL8(2)
|
0.18±0.04
|
0.12~0.16
|
-3~5
|
-5~5
|
≧400
|
≧400
|
≧300
|
|
SL-083(7)
|
0.07±0.01
|
0.26~0.42
|
-3~4
|
-3~4
|
≧150
|
≧700
|
≧500
|
Button Zn/Ag2O
|
|
SL-083(7)P
|
0.20±0.04
|
0.36~0.46
|
-3~4
|
-3~4
|
≧300
|
≧700
|
≧500
|
High capacity button Zn/Ag2O
|
|
CN-2052(3)
|
0.07±0.01
|
0.14~0.24
|
-3~5
|
-5~8
|
≧150
|
≧700
|
≧500
|
Button Zn/MnO2
|
|
CP-1
|
0.14±0.02
|
0.10~0.14
|
-3~5
|
-5~8
|
≧200
|
≧200
|
≧200
|
|
CP-2
|
0.12±0.02
|
0.08~0.12
|
-3~5
|
-5~8
|
≧200
|
≧200
|
≧200
|
* Test conditions : at 24+/-1 ºC and 1k Hz after soaked for 24 hr. in 30% KOH
|
System
|
Type
|
Thickness
* (mm)
|
Electrolyte resistance
** m
(W cm2)
|
Dry tensile strength (N/1.5cm)
|
G.M.S. g/m2
|
Pore size (mm)
|
Porosity
(%)
|
Breath ability
（ml/cm2 min）
|
Alkaline absorption (%)
|
Typical applications
|
|
Grafted
PP
Nonwoven
|
PPAS-14
|
0.140±0.025
|
0.04~0.06
|
≧5
|
25±5.0
|
≦50
|
≧50
|
≧800
|
≧400
|
Rectangular M(H)/Ni & Super capacitor
|
|
PPAS-10
|
0.100±0.025
|
0.03~0.05
|
≧5
|
18±4.0
|
≦50
|
≧50
|
≧800
|
≧400
|
|
Grafted micropore PP
membrane
|
GP-2-BS
|
0.040±0.005
|
0.08~0.13
|
≧800
|
20.0±3
|
≦6
|
≧30
|
≧15
|
≧80
|
Zn/Ni battery
|
|
PP film
|
L-B-04
|
0.037±0.005
|
|
≧800
|
|
|
|
|
|
Forming underlay of Li electrode
|
|
Non-woven PP***
|
L -16T2
|
0.160±0.025
|
|
≧3
|
40.0±5.5
|
≦50
|
≧65
|
|
|
Button Li / MnO2
|
|
L -10T
|
0.100±0.020
|
|
≧3
|
22.0± 4.0
|
≦50
|
≧65
|
|
|
|
L -12T
|
0.120±0.025
|
|
≧3
|
30.0± 4.0
|
≦50
|
≧65
|
|
|
|
L -20T
|
0.200±0.035
|
|
≧3
|
45.0± 6.0
|
≦50
|
≧65
|
|
|
* Options are available on thickness
** Test conditions: at 24±1 ºC and 1k Hz after soaked for 24 hr. in 30% KOH
*** Type illustration: L - XX T＃ L, lithium battery separator XX, multiply thickness by 100 T, tape-like ＃, quantity of layer